Structure of alumina supported vanadia catalysts for oxidative dehydrogenation of propane prepared by flame spray pyrolysis

Research output: Contribution to journalJournal article – Annual report year: 2013Researchpeer-review

View graph of relations

A series of five vanadia on alumina catalysts for oxidative dehydrogenation of propane to propene were synthesized by flame spray pyrolysis (FSP) using vanadium(III)acetylacetonate and aluminium(III)acetylacetonate dissolved in toluene as precursors. The vanadium loading was 2, 3, 5, 7.5 and 10wt.%. The catalysts were subsequently characterized by BET surface area, X-ray diffraction (XRD), Raman, UV–vis diffuse reflectance and X-ray absorption spectroscopy (XAS) as well as measurement of the catalytic performance. The catalysts had specific surface areas from 143 to 169 m2/g corresponding to average particles diameters from 9.0 to 10.9nm and apparent vanadia surface densities from 1.4 to 8.4 VOx/nm2. The only crystalline phase detected by XRD was γ-Al2O3, except at 10wt.% vanadium where traces of crystalline vanadia were observed. Raman spectroscopy showed vanadia monomers at 2 and 3wt.% V (1.4 and 2.1 VOx/nm2), a mixture of vanadia oligomers and monomers at 5wt.% V (3.6 VOx/nm2) and mainly oligomers at 7.5 and 10wt.% V (6.0 and 8.4 VOx/nm2). Diffuse reflectance UV–vis and extended X-ray absorption fine structure (EXAFS) spectroscopy measurements supported the results of Raman spectroscopy. In situ X-ray absorption near edge structure (XANES) spectroscopy showed that the vanadia can be reduced when operating at low oxygen concentrations. The catalyst performance was determined in fixed bed reactors with an inlet gas composition of C3H8/O2/N2=5/25/70. The main products were propene, CO and CO2, with traces of ethene and acrolein. Comparing propene selectivity as function of propane conversion the most selective catalysts were the 2 and 3wt.% V samples, which contained mostly vanadia monomers according to Raman spectroscopy. The best propene yield of 12% was obtained with the 2wt.% vanadium catalyst while the best space time yield of 0.78gpropene/(gcat·h) at 488°C was obtained with the 3wt.% V catalyst.
Original languageEnglish
JournalApplied Catalysis A: General
Volume451
Pages (from-to)207-215
ISSN0926-860X
DOIs
Publication statusPublished - 2013
CitationsWeb of Science® Times Cited: No match on DOI

    Research areas

  • Flame spray pyrolysis, Vanadia, Oxidative dehydrogenation, Propane, Propene, Nanoparticle
Download as:
Download as PDF
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
Word

ID: 52352580