Tantalum oxide thin films as protective coatings for sensors.

Research output: Contribution to journalJournal article – Annual report year: 1999Researchpeer-review

View graph of relations

Reactively sputtered tantalum oxide thin films have been investigated as protective coatings for aggressive media exposed sensors.

Tantalum oxide is shown to be chemically very robust. The etch rate in aqueous potassium hydroxide with pH 11 at 140°C is lower than 0.008 Å h-l. Etching in liquids with pH values in the range from pH 2 to 11 have generally given etch rates below 0.04 Å h-l. On the other hand patterning is possible in hydrofluoric acid. Further, the passivation behaviour of amorphous tantalum oxide and polycrystalline Ta2O5 is different in buffered hydrofluoric acid.

By ex situ annealing O2 in the residual thin-film stress can be altered from compressive to tensile and annealing at 450°C for 30 minutes gives a stress-free film.

The step coverage of the sputter deposited amorphous tantalum oxide is reasonable, but metallization lines are hard to cover.

Sputtered tantalum oxide exhibits high dielectric strength and the pinhole density for 0.5 μm thick films is below 3 cm-2.

Original languageEnglish
JournalJournal of Micromechanics and Microengineering
Volume9
Issue number2
Pages (from-to)113-118
ISSN0960-1317
DOIs
Publication statusPublished - 1999
CitationsWeb of Science® Times Cited: No match on DOI
Download as:
Download as PDF
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
Word

ID: 3400233