The influence of applied tensile stress on power loss in Co-rich amorphous Co-Fe-Si-B ribbons with induced magnetic anisotropy

H Nielsen, K Nielsen, Otto V Nielsen

    Research output: Contribution to journalJournal articleResearchpeer-review

    360 Downloads (Pure)

    Abstract

    The influence on power loss PTof applied tensile stress σ in amorphous (Co0.89Fe0.11)72Mo3Si15B10(lambda_{s} > 0) and Co73Mo2Si15B10(lambda_{s} <0) ribbons with different induced magnetic anisotropy Kuis reported. The losses are measured under sinusoidal flux conditions atf = 50Hz,J_{max} = 0.57T and atf = 400Hz,J_{max} = 0.10T. Measurements are carried out on samples in a stress-relieved state and with magnetic anisotropies induced by stress or field annealing. Atf = 50Hz, a minimum m Ptversus σ is observed. The σ-value (sigma_{min}) corresponding to the minimum PTincreases with increasing |Ku|. Atf = 400Hz, a minimum in PTversus σ is observed in the samples with induced magnetic anisotropy, whereassigma_{min} = 0in the stress-relieved samiales. However, no correlation between andsigma_{min}and Kuis possible from the present data.
    Original languageEnglish
    JournalI E E E Transactions on Magnetics
    Volume18
    Issue number3
    Pages (from-to)904-907
    ISSN0018-9464
    DOIs
    Publication statusPublished - 1982

    Bibliographical note

    Copyright 1982 IEEE. Personal use of this material is permitted. However, permission to reprint/republish this material for advertising or promotional purposes or for creating new collective works for resale or redistribution to servers or lists, or to reuse any copyrighted component of this work in other works must be obtained from the IEEE.

    Cite this