Surface characterisation of ethylene-propylene-diene rubber upon exposure to aqueous acidic solution

S. Mitra, Afshin Ghanbari-Siahkali, P. Kingshott, Søren Hvilsted, K. Almdal

Research output: Contribution to journalJournal articleResearchpeer-review

Abstract

Two types of pure ethylene propylene diene rubbers were exposed to two different acids for varying period of time. Surface characterisation was carried out using X-ray photoelectron spectroscopy (XPS). Two EPDM rubbers selected for this study were comparable in co-monomer compositions but significantly different with respect to molar mass and the presence of long chain branching. Both rubbers contained 5-ethylidene-2-norbomene (ENB) as diene. Solution cast films of pure EPDM samples were exposed in two different acidic solutions, viz. chromosulphuric (Cr (VI)/H2SO4) and sulphuric acid (H2SO4) (20%, v/v) at ambient temperature from 1 to 12 weeks. XPS analysis indicated that several oxygenated species were formed on the surface of both rubbers after exposure. It was postulated from the XPS analyses that both aqueous acidic solutions attacked the olefinic double bonds (C=C) of ENB. Furthermore, 20% Cr (VI)/H2SO4 also attacked the allylic carbon-hydrogen (C-H) bonds of ENB resulting in more oxygenated species on the surface compared to 20% H2SO4 under identical conditions. Cr (VI) in the 20% Cr (VI)/H2SO4 was found to play an important role in alteration of surface chemistry. Studies using a model system consisting of EPDM mixed with Cr (VI) and Cr (III) salts revealed that the change of oxidation state from Cr (VI) to Cr (III) as a consequence of direct involvement of Cr (VI) in the chemical alteration of EPDM surfaces. Interestingly, the presence of long chain branching and molar mass did not significantly influence the chemical processes owing to the acid treatment.
Original languageEnglish
JournalApplied Surface Science
Volume252
Issue number18
Pages (from-to)6280-6288
ISSN0169-4332
DOIs
Publication statusPublished - 2006

Keywords

  • EPDM
  • surface characterisation
  • elastomer
  • X-ray photoelectron spectroscopy (XPS)

Fingerprint Dive into the research topics of 'Surface characterisation of ethylene-propylene-diene rubber upon exposure to aqueous acidic solution'. Together they form a unique fingerprint.

Cite this