Structural Transition and Magnetic Field Induced Strain in Ni50Mn26.5Ga23.5 Alloy

Ngo Van Nong, Michitaka Ohtaki

Research output: Contribution to journalJournal articleResearchpeer-review

Abstract

Polycrystalline samples of Ni50Mn26.5Ga23.5 were prepared by arc-melting method. The structural transformation from tetragonal to cubic was observed from X-ray diffraction analysis as a function of temperature in the temperature range from 100 K to 370 K. Thermal magnetization curves measured at a low magnetic field of 300 Oe showed a sharp structural transformation at TM = 260 K and a magnetic transition at Curie temperature TC = 375 K. Thermal expansions were investigated in the vicinity of TM after different cooling procedures: zero-field-cooling (ZFC) and field-cooling (FC). A magnetic-field-induced strain (MFIS) of ~0.2 % obtained from the difference between the ZFC and FC thermal expansions curves is remarkable.
Original languageEnglish
JournalEngeering Sciences Reports, Kyushu University
Volume28
Issue number2
Pages (from-to)237-239
ISSN1346-7883
Publication statusPublished - 2006
Externally publishedYes

Fingerprint Dive into the research topics of 'Structural Transition and Magnetic Field Induced Strain in Ni50Mn26.5Ga23.5 Alloy'. Together they form a unique fingerprint.

Cite this