Sintering and grain growth kinetics in La0.85Sr0.15MnO3–Ce0.9Gd0.1O1.95 (LSM–CGO) porous composite

Research output: Contribution to journalJournal article – Annual report year: 2014Researchpeer-review

View graph of relations

The sintering kinetics in La0.85Sr0.15MnO3–Ce0.9Gd0.1O1.95 (LSM–CGO) porous composite was studied by applying a two-stage master sintering curve (MSC) approach and comparing with LSM and CGO single-phase materials. In the two-stage MSC, sintering mechanisms occurring at different stages were separated with respect of density, giving a typical apparent activation energy values for each sintering stage of the LSM–CGO system. Compared with the single-phase materials, retardant effect of the different phases on mass diffusion leads to much higher apparent activation energy for densification of the composite. Similarly, constrain effect was also observed in grain growth in the composite. Particularly, in the investigated temperature range (1100–1250°C), the determined grain boundary mobility of CGO in the LSM–CGO composite (10−18–10−16m3N−1s−1) is comparable with the single-phase CGO, while the grain boundary mobility of LSM in the composite (10−17–10−16m3N−1s−1) is around 1 order of magnitude smaller than the single-phase LSM.
Original languageEnglish
JournalJournal of the European Ceramic Society
Volume34
Issue number15
Pages (from-to)3769-3778
Number of pages10
ISSN0955-2219
DOIs
Publication statusPublished - 2014
CitationsWeb of Science® Times Cited: No match on DOI

    Research areas

  • Sintering, Densification, Grain growth, Ce0.9Gd0.1O1.95, La0.85Sr0.15MnO3

ID: 98562029