Root Causes and Mechanisms of Failure of Wind Turbine Blades: Overview

Leon Mishnaevsky Jr.*

*Corresponding author for this work

Research output: Contribution to journalReviewpeer-review

216 Downloads (Pure)

Abstract

A review of the root causes and mechanisms of damage and failure to wind turbine blades is presented in this paper. In particular, the mechanisms of leading edge erosion, adhesive joint degradation, trailing edge failure, buckling and blade collapse phenomena are considered. Methods of investigation of different damage mechanisms are reviewed, including full scale testing, post-mortem analysis, incident reports, computational simulations and sub-component testing. The most endangered regions of blades include the protruding parts (tip, leading edges), tapered and transitional areas and bond lines/adhesives. Computational models of different blade damage mechanisms are discussed. The role of manufacturing defects (voids, debonding, waviness, other deviations) for the failure mechanisms of wind turbine blades is highlighted. It is concluded that the strength and durability of wind turbine blades is controlled to a large degree by the strength of adhesive joints, interfaces and thin layers (interlaminar layers, adhesives) in the blade. Possible solutions to mitigate various blade damage mechanisms are discussed.
Original languageEnglish
Article number2959
JournalMaterials
Volume15
Issue number9
Number of pages29
ISSN1996-1944
DOIs
Publication statusPublished - 2022

Keywords

  • Wind energy
  • Wind turbine blades
  • Maintenance
  • Structural health monitoring

Fingerprint

Dive into the research topics of 'Root Causes and Mechanisms of Failure of Wind Turbine Blades: Overview'. Together they form a unique fingerprint.

Cite this