Rheological and thermodunamic behaviors of different calcium aluminosilicate melts with the same non-bridging oxygen content

The relationships between the chemical composition and the derivative rheological and thermodynamic values have been determined for two melt series in the anorthite-wollastonite-gehlenite (An-Wo-Geh) compatibility triangle. The melt series have 0.5 and 1 non-bridging oxygens per tetrahedrally coordinated cation (NBO/T), respectively. The influences of the ratio Si/(Si+AlCa _1/2) and NBO/T on the fragility and the configurational entropy at T_g are evaluated. Linear dependencies of the viscosity, the glass transition temperature and the fragility on the ratio Si/(Si+AlCa_1/2) are found for the two melt series. A crossover in the viscosity-temperature relationship is observed for both series, i.e. an inverse compositional dependence of viscosity in the high and low viscous range. The crossover presumably reflects different responses of the adjustment of melt structure to the substitution of Al³⁺+1/2Ca²⁺ for Si⁴⁺ in the low versus the high viscous ranges. The crossover shifts to higher temperature with increasing NBO/T.