Probing the chemistry of adhesion between a 316L substrate and spin-on-glass coating

Research output: Contribution to journalJournal article – Annual report year: 2018Researchpeer-review

Documents

DOI

View graph of relations

Hydrogen silsesquioxane ([HSiO3/2]n) based "spin-on-glass" has been deposited on 316L substrate and cured in Ar/H2 gas atmosphere at 600 ºC to form a continuous surface coating with sub-micrometer thickness. The coating functionality depends primarily on the adhesion to the substrate, which is largely affected by the chemical interaction at the interface between the coating and the substrate. We have investigated this interface by transmission electron microscopy and electron energy loss spectroscopy. The analysis identified a 5-10 nm thick interaction zone containing signals from O, Si, Cr and Fe. Analysis of the energy loss near edge structure of the present elements identified predominantly signal from [SiO4]4- units together with Fe2+, Cr2+ and traces of Cr3+. High-resolution transmission electron microscopy images of the interface region confirm a crystalline Fe2SiO4 interfacial region. In agreement with computational thermodynamics, it is proposed that the spin-on-glass forms a chemically bonded silicate-rich interaction zone with the substrate. It was further suggested that this zone is composed of a corundum-type oxide at the substrate surface, followed by an olivine-structure intermediate phase and a spinel-type oxide in the outer regions of the interfacial zone.
Original languageEnglish
JournalLangmuir
Volume34
Issue number10
Pages (from-to)3170-3176
ISSN0743-7463
DOIs
Publication statusPublished - 2018
CitationsWeb of Science® Times Cited: No match on DOI
Download as:
Download as PDF
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
Word

Download statistics

No data available

ID: 143900848