Preparing superconducting nanopowder based YBCO/Ag tapes

P. Paturi; J. Raittila; J.C. Grivel; H. Huhtinen; B. Seifi; R. Laiho; N.H. Andersen

doi:10.1016/S0921-4534(02)00905-X

Preparing superconducting nanopowder based YBCO/Ag tapes

P. Paturi, J. Raittila, J.C. Grivel, H. Huhtinen, B. Seifi, R. Laiho, N.H. Andersen

Research output: Contribution to journal › Journal article › Research › peer-review

Abstract

YBCO nanopowder consisting of 1-3 nm thick and 40 nm wide particles has been used to make silver clad superconducting tapes. After annealing in nitrogen at 945 degreesC for 10 h a critical current of 5.02 A (3300 A/cm(2)) was attained, Annealing in mixed atmosphere of oxygen and nitrogen was also carried out and this procedure produced tapes with a critical current of 2.83 A (2200 A/cm(2)). These tapes show very good characteristics in magnetic fields. (C) 2002 Elsevier Science B.V. All rights reserved.

Original language	English
Journal	Physica C: Superconductivity and its Applications
Volume	372-376
Pages (from-to)	779-781
ISSN	0921-4534
DOIs	https://doi.org/10.1016/S0921-4534(02)00905-X
Publication status	Published - 2002

Access to Document

10.1016/S0921-4534(02)00905-X

OpenUrl availability

Full text

Cite this

@article{78af30755f554072a7e996c3fe7d60f3,

title = "Preparing superconducting nanopowder based YBCO/Ag tapes",

abstract = "YBCO nanopowder consisting of 1-3 nm thick and 40 nm wide particles has been used to make silver clad superconducting tapes. After annealing in nitrogen at 945 degreesC for 10 h a critical current of 5.02 A (3300 A/cm(2)) was attained, Annealing in mixed atmosphere of oxygen and nitrogen was also carried out and this procedure produced tapes with a critical current of 2.83 A (2200 A/cm(2)). These tapes show very good characteristics in magnetic fields. (C) 2002 Elsevier Science B.V. All rights reserved. ",

keywords = "5-I nano",

author = "P. Paturi and J. Raittila and J.C. Grivel and H. Huhtinen and B. Seifi and R. Laiho and N.H. Andersen",

year = "2002",

doi = "10.1016/S0921-4534(02)00905-X",

language = "English",

volume = "372-376",

pages = "779--781",

journal = "Physica C: Superconductivity and its Applications",

issn = "0921-4534",

publisher = "Elsevier",

}

TY - JOUR

T1 - Preparing superconducting nanopowder based YBCO/Ag tapes

AU - Paturi, P.

AU - Raittila, J.

AU - Grivel, J.C.

AU - Huhtinen, H.

AU - Seifi, B.

AU - Laiho, R.

AU - Andersen, N.H.

PY - 2002

Y1 - 2002

N2 - YBCO nanopowder consisting of 1-3 nm thick and 40 nm wide particles has been used to make silver clad superconducting tapes. After annealing in nitrogen at 945 degreesC for 10 h a critical current of 5.02 A (3300 A/cm(2)) was attained, Annealing in mixed atmosphere of oxygen and nitrogen was also carried out and this procedure produced tapes with a critical current of 2.83 A (2200 A/cm(2)). These tapes show very good characteristics in magnetic fields. (C) 2002 Elsevier Science B.V. All rights reserved.

AB - YBCO nanopowder consisting of 1-3 nm thick and 40 nm wide particles has been used to make silver clad superconducting tapes. After annealing in nitrogen at 945 degreesC for 10 h a critical current of 5.02 A (3300 A/cm(2)) was attained, Annealing in mixed atmosphere of oxygen and nitrogen was also carried out and this procedure produced tapes with a critical current of 2.83 A (2200 A/cm(2)). These tapes show very good characteristics in magnetic fields. (C) 2002 Elsevier Science B.V. All rights reserved.

KW - 5-I nano

U2 - 10.1016/S0921-4534(02)00905-X

DO - 10.1016/S0921-4534(02)00905-X

M3 - Journal article

SN - 0921-4534

VL - 372-376

SP - 779

EP - 781

JO - Physica C: Superconductivity and its Applications

JF - Physica C: Superconductivity and its Applications

ER -

Preparing superconducting nanopowder based YBCO/Ag tapes

Abstract

Access to Document

OpenUrl availability

Fingerprint

Cite this