Phosphoric acid doped polysulfone membranes with aminopyridine pendant groups and imidazole cross-links

Research output: Contribution to journalJournal article – Annual report year: 2015Researchpeer-review

View graph of relations

Udel polysulfone based membranes with 4-aminopyridine pendant groups and cross-linking imidazole units are synthesized in a simple two step reaction. The ratio of 4-aminopyridine and imidazole is varied and the materials are extensively characterized. The average phosphoric acid uptake (in 85 wt% PA) ranges between 90 wt% and 452 wt% depending on the ratio of 4-aminopyridine and imidazole and the membranes show good proton conductivity of up to 65 mS cm-1 at 160 °C under non-humidified conditions. The applicability of these materials as a polymer electrolyte membrane was proven by single cell tests at 130 °C. The relationships between PA uptake, chemical composition and mechanical stability are reported. Proton conductivity and mechanical properties only depend on the phosphoric acid content, which, however is a function of the chemical composition.
Original languageEnglish
JournalEuropean Polymer Journal
Volume72
Pages (from-to)102-113
Number of pages12
ISSN0014-3057
DOIs
Publication statusPublished - 2015
CitationsWeb of Science® Times Cited: No match on DOI

    Research areas

  • High temperature polymer electrolyte membrane fuel cell (HT-PEMFC), Udel polysulfone, Aminopyridine