Microstructure degradation of LSM-YSZ cathode in SOFCs operated at various conditions

Keyphrases

• Degradation Process 100%
• Cell Test 100%
• LSM Cathode 100%
• Microstructure Degradation 100%
• Interface Stability 100%
• Degradation Mechanism 50%
• Current Density 50%
• Microstructural Analysis 50%
• Operating Parameters 50%
• Load Current 50%
• Cell Voltage 50%
• Degradation Rate 50%
• Cathode Microstructure 50%
• High Current Density 50%
• Cell Operation 50%
• Voltage Degradation 50%
• Grain Coarsening 50%
• Cathode Degradation 50%
• Element Diffusion 50%
• Cathode-electrolyte Interface 50%

Material Science

• Cathode 100%
• Density 40%
• Coarsening 20%
• Microstructural Analysis 20%
• Sintering 20%