meta-PBI/methylated PBI-OO blend membranes for acid doped HT PEMFC

Research output: Contribution to journalJournal article – Annual report year: 2014Researchpeer-review

View graph of relations

Methylation of polybenzimidazole leads to positively charged polymer backbones, and moveable anions. Ion exchange of methylated PBI-OO in phosphoric acid (PA) shows that the resulting polymers dissolve. meta-PBI, however, absorbs about 400wt% PA while remaining a self supported membrane. We investigate the properties of blend membranes, employing meta-PBI for mechanical integrity and methylated PBI-OO for high PA uptake and resulting proton conductivity. While small additions of PBI-OO decrease the tensile strength of blend membranes (58MPa for 10% PBI-OO), further addition leads to an increase, and 50% blend membranes show again a tensile strength of 74MPa, just 3MPa lower than pure meta-PBI membranes. Thermal stability of iodide exchanged blend membranes appears to be remarkably high, probably because cleaved iodomethane does not evaporate but methylates meta-PBI. PA concentration in doped membranes of 60–63% is reached by doping in 60% PA (blend; 6.3PA/repeat unit) and 70% PA (meta-PBI; 4.6PA/r.u.). This suggests that blends absorb PA more strongly. Both membranes show similar conductivity between rt and 140°C, indicating that PA concentration describes these membranes better than PA/r.u. In the fuel cell, blend membranes show similar or better performance than meta-PBI. In the TGA, blends doped in 20% PA showed a stable plateau between 115 and 180°C, while meta-PBI lost weight continuously.
Original languageEnglish
JournalEuropean Polymer Journal
Volume58
Pages (from-to)135-143
ISSN0014-3057
DOIs
Publication statusPublished - 2014
CitationsWeb of Science® Times Cited: No match on DOI

    Research areas

  • Polybenzimidazole, Blend membranes, Methylated PBI-OO, Polybenzimidazolium, Phosphoric acid doping, High temperature polymer electrolyte fuel cell