Abstract
A partially recrystallized copper sample produced by cold-rolling and annealing was
deformed in situ by uniaxial tension in a scanning electron microscope, and electron backscatter
diffraction data were collected before and after deformation to certain strains. The local strain
distributions are quantified using digital image correlation. Distributions of the normal strain
along the tensile direction (εxx) are shown in this paper. The recrystallized grains are found to
deform more than the remaining unrecrystallized matrix. When εxx is averaged along lines
perpendicular to the tensile direction, significant variation are observed, which may be related
to the local recrystallized volume fraction.
Original language | English |
---|---|
Article number | 012103 |
Journal | I O P Conference Series: Materials Science and Engineering |
Volume | 82 |
Number of pages | 4 |
ISSN | 1757-8981 |
DOIs | |
Publication status | Published - 2015 |
Event | 17th International Conference on Textures of Materials - Dresden, Germany Duration: 24 Aug 2014 → 29 Aug 2014 Conference number: 17 http://www.icotom17.com/?node=1 |
Conference
Conference | 17th International Conference on Textures of Materials |
---|---|
Number | 17 |
Country/Territory | Germany |
City | Dresden |
Period | 24/08/2014 → 29/08/2014 |
Internet address |