In situ characterization of delamination and crack growth of a CGO–LSM multi-layer ceramic sample investigated by X-ray tomographic microscopy

Research output: Contribution to journalJournal article – Annual report year: 2014Researchpeer-review

View graph of relations

The densification, delamination and crack growth behavior in a Ce0.9Gd0.1O1.95 (CGO) and (La0.85Sr0.15)0.9MnO3 (LSM) multi-layer ceramic sample was studied using in situ X-ray tomographic microscopy (microtomography) to investigate the critical dynamics of crack propagation and delamination in a multilayered sample. Naturally occurring defects, caused by the sample preparation process, are shown not to be critical in sample degradation. Instead defects are nucleated during the debinding step. Crack growth is significantly faster along the material layers than perpendicular to them, and crack growth and delamination only accelerates when sintering occurs.
Original languageEnglish
JournalJournal of the European Ceramic Society
Volume34
Issue number12
Pages (from-to)3019-3025
ISSN0955-2219
DOIs
Publication statusPublished - 2014
CitationsWeb of Science® Times Cited: No match on DOI

    Research areas

  • Sintering, Tomography, Multi-layer, Crack growth, Delamination

Download statistics

No data available

ID: 93075657