Abstract
Four modified aluminide coatings were prepared on superalloy DZ38G, which include a two step co-cementation coating NiCr-CrAl and three one step co-cementation coatings Co-Al, AlSi and Al-Ti. Then their microstructure and hot corrosion behavior in a salt melt of 25%NaCl (mass fraction)+75%Na2SO4 (mass fraction) at 900 ℃ were investigated. The results show that a continuously compact scale of corrosion products with good adhesion to the matrix could form on Ti-Al coating during corrosion, therefore, the Al- Ti coating may provide much better protectiveness to the alloy rather than the other three coatings in this kind of salt mixture.
| Original language | Chinese |
|---|---|
| Journal | Journal of Chinese Society for Corrosion and Protection |
| Volume | 34 |
| Issue number | 6 |
| Pages (from-to) | 502-506 |
| DOIs | |
| Publication status | Published - 2014 |
| Externally published | Yes |
Keywords
- Superalloy
- Coating
- Hot Corrosion
Cite this
- APA
- Author
- BIBTEX
- Harvard
- Standard
- RIS
- Vancouver