Fatigue damage propagation in unidirectional glass fibre reinforced composites made of a non-crimp fabric

Jens Zangenberg Hansen, Povl Brøndsted, John W. Gillespie Jr.

Research output: Contribution to journalJournal articleResearchpeer-review

Abstract

Damage progression in unidirectional glass fibre reinforced composites manufactured of a non-crimp fabric subjected to tension-tension fatigue is investigated, and a quantitative explanation is given for the experimentally observed stiffness degradation. The underlying damage-mechanisms are examined using three distinct microscopic analyses, and the transverse crack density is measured. It is documented that the stiffness loss in fatigue is directly related to fibre fractures in the load-carrying axial fibre bundles, initialised by interface debonding and cracking in the transverse backing bundles.
A simple stiffness spring model validates the stiffness loss observed. A fatigue damage scheme is presented, which suggests that damage initiates due to failure of the backing bundle causing a stress concentration in the axial load carrying fibres. This stress concentration, along with fretting fatigue, gives rise to axial fibre fractures and a loss of stiffness, eventually leading to final failure. The uniqueness of the present work is identification of the mechanisms associated with tension fatigue failure of unidirectional non-crimp fabrics used for wind turbine blades. The observed damage mechanisms need further attention and understanding in order to improve the fatigue life-time of unidirectional glass fibre reinforced non-crimp fabrics.
Original languageEnglish
JournalJournal of Composite Materials
Volume48
Issue number22
Pages (from-to)2711-2727
ISSN0021-9983
DOIs
Publication statusPublished - 2014
EventECCM15: 15th European Confeernce on Composite Materials - Venica, Italy
Duration: 24 Jun 201228 Jun 2012
http://www.eccm15.org/

Conference

ConferenceECCM15
CountryItaly
CityVenica
Period24/06/201228/06/2012
Internet address

Keywords

  • Fatigue damage
  • Glass fibre reinforced composite
  • Fibre fracture
  • Microscopy
  • Stiffness degradation
  • Non-crimp fabric

Fingerprint Dive into the research topics of 'Fatigue damage propagation in unidirectional glass fibre reinforced composites made of a non-crimp fabric'. Together they form a unique fingerprint.

Cite this