Fabrication of thin yttria-stabilized-zirconia dense electrolyte layers by inkjet printing for high performing solid oxide fuel cells

Research output: Contribution to journalJournal article – Annual report year: 2015Researchpeer-review

View graph of relations

In this work, we present how a low-cost HP Deskjet 1000 inkjet printer was used to fabricate a 1.2 mm thin, dense and gas tight 16 cm2 solid oxide fuel cells (SOFC) electrolyte. The electrolyte was printed using an ink made of highly diluted (<4 vol.%) nanometric yttria stabilized zirconia (YSZ) powders (50 nm in size) in an aqueous medium. The ink was designed to be a highly dispersed, long term stable colloidal suspension, with optimal printability characteristics. The electrolyte was made by a multiple printing procedure, which ensures coverage of the several flaws occurring in a single printing pass. Together with an optimized sintering procedure this resulted in good adhesion and densification of the electrolyte. The SOFC exhibited a close-to-theoretical open circuit voltage and a remarkable peak power density above 1.5 W cm-2 at 800 °C.
Original languageEnglish
JournalJournal of Power Sources
Volume273
Pages (from-to)89-95
ISSN0378-7753
DOIs
Publication statusPublished - 2015
CitationsWeb of Science® Times Cited: No match on DOI

    Research areas

  • SOFC, Inkjet printing, YSZ, Colloidal suspension

ID: 100630805