Epitaxial growth of YBa2Cu3O7−x films on Ce0.9La0.1O2−y buffered yttria-stabilized zirconia substrates by an all-chemical-solution route

Zhao Yue, Wei Wu, Xiao Tang, Niels Hessel Andersen, Zhenghe Han, Jean-Claude Grivel

Research output: Contribution to journalJournal articleResearchpeer-review

Abstract

In view of high rate fabrication of coated conductors at low-cost, YBa2Cu3O7 (YBCO) films on Ce0.9La0.1O2−y buffered yttria-stabilized zirconia substrates were deposited by means of a novel low-fluorine metal–organic solution route. A high critical current density of 3 MA cm−2 (77 K, self field) was achieved on such an all-chemical derived configuration. Structural characterization showed that the enhanced superconductivity performance of the YBCO films is mainly related to the defects induced by the interface.
Original languageEnglish
JournalCrystEngComm
Volume16
Issue number21
Pages (from-to)4369 – 4372
Number of pages4
ISSN1466-8033
DOIs
Publication statusPublished - 2014

Fingerprint Dive into the research topics of 'Epitaxial growth of YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7−x</sub> films on Ce<sub>0.9</sub>La<sub>0.1</sub>O<sub>2−y</sub> buffered yttria-stabilized zirconia substrates by an all-chemical-solution route'. Together they form a unique fingerprint.

Cite this