Densification of Highly Defective Ceria by High Temperature Controlled Re-Oxidation

Research output: Contribution to journalJournal article – Annual report year: 2014Researchpeer-review

View graph of relations

Highly enhanced densification and grain growth of Ce0.9Gd0.1O1.95-δ (CGO, gadolinium-doped ceria, with 10 mol% Gd) is achieved in low oxygen activity atmospheres. However, the material can suffer mechanical failures during cooling when the re-oxidation process is not controlled due to the large volume changes. In this work, the redox process of CGO is investigated using dilatometry, microscopy, electrochemical impedance spectroscopy and thermodynamic analysis. In addition, the conditions allowing controlled re-oxidation and cooling in order to preserve the mechanical integrity of the CGO component are defined: this can be achieved over a wide temperature range (800−1200◦C) by gradually increasing the oxygen content of the atmosphere. It is found that the electrical conductivity of the CGO, particularly at low temperature (<450◦C) is influenced by the sintering and controlled re-oxidation conditions. An increase in activation energy for conduction at low temperature is observed as the re-oxidation temperature decreases. Moreover it was observed that the ionic conductivity blocking effect, usually associated with grain boundary contributions, is not influenced by the grain size but rather by the chemical history of the material. © 2014 The Electrochemical Society.
Original languageEnglish
JournalJournal of The Electrochemical Society
Volume161
Issue number11
Pages (from-to)F3072-F3078
ISSN0013-4651
DOIs
Publication statusPublished - 2014
CitationsWeb of Science® Times Cited: No match on DOI

ID: 100010739