Crystallographic dependence of the lateral undercut wet etch rate of Al0.5In0.5P in diluted HCl for III-V sacrificial release

Research output: Contribution to journalJournal article – Annual report year: 2013Researchpeer-review

View graph of relations

The authors investigated the use of InAlP as a sacrificial layer lattice-matched to GaAs when diluted hydrochloric acid is used for sacrificial etching. They show that InAlP can be used to fabricate submicrometer air gaps in micro-opto-electro-mechanical systems and that a selectivity toward GaAs larger than 500 is achieved. This selectivity enables fabrication control of the nanometer-size structures required in photonic crystal and high-index contrast subwavelength grating structures. The crystallographic dependence of the lateral etch rate in InAlP is shown to be symmetric around the 〈110〉 directions where an etch rate of 0.5 μm/min is obtained at 22 °C in HCl:2H2O. Since the etch rate in the 〈100〉 directions exceeds by ten times that of the 〈110〉 directions, InAlP may be used in sacrificial release of high-aspect ratio structures. Free-hanging structures with length to air-gap aspect ratios above 600 are demonstrated by use of critical point drying following the sacrificial etch.
Original languageEnglish
JournalJournal of Vacuum Science and Technology. Part B. Microelectronics and Nanometer Structures
Volume31
Issue number1
Pages (from-to)011209
Number of pages4
ISSN1071-1023
DOIs
Publication statusPublished - 2013

Bibliographical note

Copyright (2013) American Institute of Physics. This article may be downloaded for personal use only. Any other use requires prior permission of the author and the American Institute of Physics. The following article appeared in J. Vac. Sci. Technol. B 31, 011209 (2013) and may be found at http://avspublications.org/jvstb/resource/1/jvtbd9/v31/i1/p011209_s1.

CitationsWeb of Science® Times Cited: No match on DOI

    Research areas

  • indium compounds

Download statistics

No data available

ID: 51977865