Corrosion behavior and conductivity of TiNb and TiNbN Coated Steel For Metallic Bipolar Plates

Research output: Contribution to journalJournal article – Annual report year: 2019Researchpeer-review

Documents

DOI

View graph of relations

To improve corrosion resistance and electronic conductivity of bipolar plates for proton exchange membrane fuel cells (PEMFC), coatings of TiNb and TiNbN on 316L stainless steel (SS) were prepared by magnetron sputtering. X-ray diffraction measurements confirmed the existence of metallic nitrides in the TiNbN coating. Scanning electron microscope tests showed that the deposited coatings provided smooth surfaces. Further electrochemical measurements indicated that the corrosion resistance of the TiNb coating was significantly higher than that of the substrate. At 0.19 V vs MSE, the long-term stabilized current density of TiNb/316L SS was lower than 1 μA·cm-2. The interfacial contact resistance values between coating and carbon paper suggested that TiNb and TiNbN films had better contact conductivity than the 316L SS substrate. In conclusion, TiNb coated 316L SS metallic bipolar plate material is a promising option for PEMFC.
Original languageEnglish
Article number2568
JournalApplied Sciences (switzerland)
Volume9
Issue number12
Number of pages12
ISSN2076-3417
DOIs
Publication statusPublished - 2019
CitationsWeb of Science® Times Cited: No match on DOI

    Research areas

  • Coating, Metallic bipolar plate, PEMFC, TiNb, TiNbN

Download statistics

No data available

ID: 185524689