TY - JOUR
T1 - Cavity Formation in Aluminium Irradiated with a Pulsating Beam of 225 MeV Electrons
AU - Singh, Bachu Narain
AU - Bilde-Sørensen, Jørgen
AU - Leffers, Torben
AU - Ozhigou, L.S
AU - Gann, V.V.
PY - 1984
Y1 - 1984
N2 - High-purity aluminium was irradiated with a pulsating beam of 225 MeV electrons to a maximum dose of 0.035 dpa with a helium generation rate of up to 17 appm/dpa. The irradiated samples contained cavities in the size range 5 to 70 nm. In a zone of up to 14 μm from the grain boundaries cavity size and density are found to be greater than in the grain interior.
AB - High-purity aluminium was irradiated with a pulsating beam of 225 MeV electrons to a maximum dose of 0.035 dpa with a helium generation rate of up to 17 appm/dpa. The irradiated samples contained cavities in the size range 5 to 70 nm. In a zone of up to 14 μm from the grain boundaries cavity size and density are found to be greater than in the grain interior.
U2 - 10.1016/0022-3115(84)90653-6
DO - 10.1016/0022-3115(84)90653-6
M3 - Journal article
SN - 0022-3115
VL - 122
SP - 542
EP - 546
JO - Journal of Nuclear Materials
JF - Journal of Nuclear Materials
IS - 1-3
ER -