Activation/Deactivation Phenomena in the Electrochemical Reduction of Nitric oxide and Oxygen on LSM perovskites

Research output: Contribution to journalJournal article – Annual report year: 2018Researchpeer-review

Documents

DOI

View graph of relations

The effect of anodic pretreatment on LaMnO3+delta, La0.85Sr0.15MnO3+delta and La0.5Sr0.5MnO3 point electrodes were investigated using cyclic voltammetry in the temperature range 200 to 400 degrees C in either 10% oxygen in argon or 1% nitric oxide in argon. The electrodes, in most cases, were deactivated in oxygen-containing gas and activated in nitric oxide-containing gas after anodic polarization. This was thought to be due to potential-induced SrO segregation to the surface of the electrodes and annihilation of oxygen vacancies. This work shows that the effect in some cases is significant and must be considered when evaluating the electrodes. In addition, the activity of the electrodes increases with increasing strontium content with respect to the reduction of both oxygen and nitric oxide. The electrodes were all more active with respect to the reduction of nitric oxide than with respect to the reduction of oxygen in the investigated temperature range.
Original languageEnglish
JournalInternational Journal of Electrochemical Science
Volume13
Issue number5
Pages (from-to)4782-4791
ISSN1452-3981
DOIs
Publication statusPublished - 2018
CitationsWeb of Science® Times Cited: No match on DOI

    Research areas

  • LSM, NO, O2, Activation, Deactivation