Tweaking the spin-wave dispersion and suppressing the incommensurate phase in LiNiPO4 by iron substitution

Publication: Research - peer-reviewJournal article – Annual report year: 2009

NullPointerException

View graph of relations

Elastic and inelastic neutron-scattering studies of Li(Ni1−xFex)PO4 single crystals reveal anomalous spin-wave dispersions along the crystallographic direction parallel to the characteristic wave vector of the magnetic incommensurate phase. The anomalous spin-wave dispersion (magnetic soft mode) indicates the instability of the Ising-type ground state that eventually evolves into the incommensurate phase as the temperature is raised. The pure LiNiPO4 system (x=0) undergoes a first-order magnetic phase transition from a long-range incommensurate phase to an antiferromagnetic (AFM) ground state at TN=20.8 K. At 20% Fe concentrations, although the AFM ground state is to a large extent preserved as that of the pure system, the phase transition is second order, and the incommensurate phase is completely suppressed. Analysis of the dispersion curves using a Heisenberg spin Hamiltonian that includes interplane and in-plane nearest- and next-nearest-neighbor couplings reveals frustration due to strong competing interactions between nearest- and next-nearest-neighbor sites, consistent with the observed incommensurate structure. The Fe substitution only slightly lowers the extent of the frustration, sufficient to suppress the incommensurate phase. An energy gap in the dispersion curves gradually decreases with the increase in Fe content from ∼2 meV for the pure system (x=0) to ∼0.9 meV for x=0.2.
Original languageEnglish
JournalPhysical Review B (Condensed Matter and Materials Physics)
Publication date2009
Volume79
Journal number17
Pages174435
ISSN1098-0121
DOIs
StatePublished

Bibliographical note

Copyright (2009) by the American Physical Society.

CitationsWeb of Science® Times Cited: 4

Keywords

  • Materials research, Superconducting materials for the energy sector
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

Download statistics

No data available

ID: 4849362