Thermocleavable Materials for Polymer Solar Cells with High Open Circuit Voltage-A Comparative Study

Publication: Research - peer-reviewJournal article – Annual report year: 2009

View graph of relations

The search for polymer solar cells giving a high open circuit voltage was conducted through a comparative study of four types of bulk-heterojunction solar cells employing different photoactive layers. As electron donors the thermo-cleavable polymer poly-(3-(2-methylhexyloxycarbonyl)dithiophene) (P3MHOCT) and unsubstituted polythiophene (PT) were used, the latter of which results from thermo cleaving the former at 310 °C. As reference, P3HT solar cells were built in parallel. As electron acceptors, either PCBM or bis-[60]PCBM were used. In excess of 300 solar cells were produced under as identical conditions as possible, varying only the material combination of the photo active layer. It was observed that on replacing PCBM with bis[60]PCBM, the open circuit voltage on average increased by 100 mV for P3MHOCT and 200 mV for PT solar cells. Open circuit voltages approaching 1 V were observed for the PT:bis[60]PCBM solar cells and a maximum conversion efficiency of 1.3% was obtained for solar cells with P3MHOCT:PCBM as the photoactive material. For the reference solar cells maximum efficiencies of 2.1 and 2.4% were achieved for P3HT:PCBM and P3HT:bis[60]PCBM, respectively. Despite special measures taken in terms of substrate design and device processing, a substantial spread in the photovoltaic properties was generally observed. This spread could not be correlated with the optical properties of the solar cells, the thickness of the photo active layer or the electrode deposition conditions of the aluminum top electrode.
Original languageEnglish
JournalA C S Applied Materials and Interfaces
Publication date2009
Volume1
Issue12
Pages2768-2777
ISSN1944-8244
DOIs
StatePublished

Bibliographical note

This work was supported by the Danish
Strategic Research Council (DSF 2104-05-0052 and 2104-
07-0022).

CitationsWeb of Science® Times Cited: 29

Keywords

  • Polymer solar cells, Solar energy
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

ID: 4398051