The reaction of sintered aluminium products with uranium dioxide and monocarbide

Publication: Research - peer-reviewJournal article – Annual report year: 1965

View graph of relations

The compatibility of SAP 930 with uranium dioxide and uranium monocarbide was investigated in the temperature range 450–600° C. The results indicate that a severe reaction occurs between SAP 930 and UO2 within 8000 hours at 600° C, a slight reaction at 600° C for 1000 hours and after 11 900 hours at 525° C, and no reaction in 14 300 hours at 450° C. Of the three grades of UC tested (hot pressed, arc cast, cold pressed and sintered) the slightly substoichiometric, hot-pressed UC is judged to be least compatible with SAP 930, reaction occurring after 7300 hours at 450° C. No reaction was observed between SAP 930 and the other carbides at this temperature. All SAP−UC combinations are incompatible at 600° C for as little as 100 hours of heat treatment. Tests designed to study the effect of a diffusion barrier on the SAP−UC reaction have shown that anodized SAP 930 and the three uranium carbides are fully compatible at 450 and 525° C for at least 14 300 hours. Mechanical breakdown of the barrier within 8000 hours, however, limits the application of anodized SAP 930 at 600° C. X-ray diffraction analyses of the reaction products formed in each material combination tested show that the primary constituent is the intermetallic compound UAl3. A second phase, visible at the SAP/reaction-product interface, has been identified as UAl4 on the basis of its observed anisotropy and its position in the reaction zone.
Original languageEnglish
JournalJournal of Nuclear Materials
Publication date1965
Volume16
Issue2
Pages173-183
ISSN0022-3115
DOIs
StatePublished
CitationsWeb of Science® Times Cited: 2
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

ID: 5868800