Pore former induced porosity in LSM/CGO cathodes for electrochemical cells for flue gas purification

Publication: Research - peer-reviewJournal article – Annual report year: 2011

Documents

DOI

View graph of relations

In this study the effect of the characteristics of polymethyl methacrylate (PMMA) pore formers on the porosity, pore size distribution and the air flow through the prepared lanthanum strontium manganate/gadolinium-doped cerium oxide (LSM/CGO) cathodes was investigated. Porous cathodes were obtained and the highest porosity measured was 46.4% with an average pore diameter of 0.98 μm. The air flow through this cathode was measured to 5.8 ml/(min mm2). Also the effect of exposure time to the solvent was tested for the most promising PMMA pore former and it was found that the average pore diameter decreases as a result of elongated exposure. Also prolong milling of the LSM powder was found to decrease the porosity of the final cathode and milling time should be highly controlled in order to obtain as porous cathodes as possible.
Original languageEnglish
JournalCeramics International
Publication date2012
Volume38
Journal number2
Pages1751-1754
ISSN0272-8842
DOIs
StatePublished
CitationsWeb of Science® Times Cited: 4

Keywords

  • A. Tape casting, Porosities, Material preparations
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

Download statistics

No data available

ID: 6336498