Physicochemical properties of phosphoric acid doped polybenzimidazole membranes for fuel cells

Publication: Research - peer-reviewJournal article – Annual report year: 2006

View graph of relations

Polybenzimidazole (PBI) membranes have been prepared with different molecular weights. The water and acid swelling, mechanical strength,gas permeability and proton conductivity were studied for the pristine and acid doped PBI membranes. When doped with 5 mol of phosphoric acid per mole repeat unit of the polymer, a level necessary to obtain high enough proton conductivity for fuel cell uses, the polymer membrane exhibits a volume swelling by 118%, resulting in separation of the polymer backbones. The separation in turn reduces the mechanical strength of the membrane especially at high temperatures. Another consequence is the increased H2 and O2 permeability through the membrane. In the temperature range from 120 to 180 ◦C, the hydrogen permeability was found to be 1.6–4.3×10−17 and 1.2–4.0×10−15 mol cm cm−2 s−1 Pa−1 for pristine and acid doped PBI membranes, respectively, while for oxygen it was 5.0–10×10−19 and 3.0–9.4×10−16 mol cm cm−2 s−1 Pa−1,respectively. High molecular weights of the polymers improve the mechanical strength but have little influence on the proton conductivity of the membranes.
Original languageEnglish
JournalJournal of Membrane Science
Publication date2006
Volume277
Pages38-45
StatePublished
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

ID: 2454664