Phase Identification and Internal Stress Analysis of Steamside Oxides on Plant Exposed Superheater Tubes
Publication: Research - peer-review › Conference article – Annual report year: 2012
During long-term, high-temperature exposure of superheater tubes in thermal power plants, various oxides are formed on the inner side (steamside) of the tubes, and oxide spallation is a serious problem for the power plant industry. Most often, oxidation in a steam atmosphere is investigated in laboratory experiments just mimicking the actual conditions in the power plant for simplified samples. On real plant-exposed superheater tubes, the steamside oxides are solely investigated microscopically. The feasibility of X-ray diffraction for the characterization of steamside oxidation on real plant-exposed superheater tubes was proven in the current work; the challenges for depth-resolved phase analysis and phase-specific residual stress analysis at the inner side of the tubes with concave surface curvature are discussed. Essential differences between the steamside oxides formed on two different steels typically applied for superheaters, ferritic-martensitic X20CrMoV12-1 and lean austenitic stainless steel TP347H, respectively, are revealed by X-ray diffraction.
|Journal||Metallurgical and Materials Transactions A - Physical Metallurgy and Materials Science|
|State||Published - 2012|
|Event||Neutron and X-Ray Studies of Advanced Materials IV. 2011 TMS Annual Meeting & Exhibition - San Diego, CA, United States|
|Conference||Neutron and X-Ray Studies of Advanced Materials IV. 2011 TMS Annual Meeting & Exhibition|
|City||San Diego, CA|
|Period||27/02/2011 → 03/03/2011|
|Citations||Error in DOI please contact firstname.lastname@example.org|
- MATERIALS, METALLURGY, OXIDATION-KINETICS, FERRITIC STEELS, WATER-VAPOR, POWER-PLANT, TEMPERATURE, BEHAVIOR, GROWTH, STRAIN, MICROSTRUCTURE, DISTRIBUTIONS
Loading map data...
No data available