Optimizing shape uniformity and increasing structure heights of deep reactive ion etched silicon x-ray lenses: Paper

Publication: Research - peer-reviewJournal article – Annual report year: 2015

DOI

View graph of relations

Line-focusing compound silicon x-ray lenses with structure heights exceeding 300 μm were fabricated using deep reactive ion etching. To ensure profile uniformity over the full height, a new strategy was developed in which the perimeter of the structures was defined by trenches of constant width. The remaining sacrificial material inside the lens cavities was removed by etching through the silicon wafer. Since the wafers become fragile after through-etching, they were then adhesively bonded to a carrier wafer. Individual chips were separated using laser micro machining and the 3D shape of fabricated lenses was thoroughly characterized by a variety of means. Optical testing using synchrotron radiation with a photon energy of 56 keV yielded a 300 μm wide beam with a waist of 980 nm (full width at half maximum) at a focal length of 1.3 m. Optical aberrations are discussed in the context of the shape analysis, where a slight bowing of the lens sidewalls and an insufficiently uniform apex region are identified as resolution-limiting factors. Despite these, the proposed fabrication route proved a viable approach for producing x-ray lenses with large structure heights and provides the means to improve the resolution and capabilities of modern x-ray techniques such as x-ray microscopy and 3D x-ray diffraction.
Original languageEnglish
Article number125013
JournalJournal of Micromechanics and Microengineering
Volume25
Issue number12
Number of pages10
ISSN0960-1317
DOIs
StatePublished - 2015
CitationsWeb of Science® Times Cited: 2

    Keywords

  • High-aspect ratio microstructures, Deep reactive ion etching, X-ray optics, Compound refractive lenses
Download as:
Download as PDF
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
Word

ID: 117887477