Monitoring reinforcement corrosion and corrosion-induced cracking using non-destructive x-ray attenuation measurements

Publication: Research - peer-reviewJournal article – Annual report year: 2011

View graph of relations

To test the applicability of the x-ray attenuation method to monitor the movement of corrosion products as well as the formation and propagation of cracks in cementitious materials reinforced mortar samples were prepared and tested under accelerated corrosion conditions. It is evident from the experimental results that the x-ray attenuation method is suitable to track time-dependent movements of the corrosion products and the subsequent development (formation and propagation) of corrosion-induced cracks. The x-ray attenuation measurements allowed determination of the actual concentration of the corrosion products averaged through the specimen thickness. The total mass loss of steel, obtained by the x-ray attenuation method, was found to be in very good agreement with the mass loss obtained by gravimetric method as well as Faraday's law.
Original languageEnglish
JournalCement and Concrete Research
Publication date2011
Volume41
Issue11
Pages1085-1094
ISSN0008-8846
DOIs
StatePublished
CitationsWeb of Science® Times Cited: 16

Keywords

  • C. Corrosion, Non-destructive testing (NDT), B. Crack detection, B. EDX, D. Reinforcement
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

ID: 5743908