Model-based analysis of photoinitiated coating degradation under artificial exposure conditions

Publication: Research - peer-reviewJournal article – Annual report year: 2012

Documents

DOI

View graph of relations

Coating degradation mechanisms of thermoset coatings exposed to ultraviolet radiation and humidity at constant temperature are investigated. The essential processes, photoinitiated oxidation reactions, intrafilm oxygen permeability, water absorption and diffusion, reduction of crosslink density, and development of a thin surface oxidation zone are quantified and a mathematical model for degrading coatings developed. Front-tracking techniques are used to determine the rate of movement of the oxidation and ablation fronts, the positions of which define the extension of the surface oxidation zone. Three previous and independent experimental investigations with two-component, densely crosslinked, epoxy–amine model coatings were selected for verification of the mathematical model. Simulations can match and explain transient mass loss and coating thickness reduction data and are in agreement with infrared measurements of carbonyl groups formed in the surface zone. The thickness of the stable surface oxidation zone, which is established after an initial ablation lag time, is estimated by the model to 0.5–2 μm in good agreement with previous measurements. Simulated concentration profiles of active groups, oxygen, and radicals in the stable surface oxidation zone are presented and analyzed. The mathematical model can be used for obtaining a quantitative insight into the degradation of thermoset coatings and has potential, after further development, to complete commercial coatings and dynamic exposure conditions, to become a supplementing tool for predicting in-service coating behavior based on accelerated laboratory measurements.
Original languageEnglish
JournalJournal of Coatings Technology and Research
Publication date2012
Volume9
Issue4
Pages375-398
ISSN1547-0091
DOIs
StatePublished

Bibliographical note

Copyright The Author 2011. This article is published with open access at Springerlink.com

CitationsWeb of Science® Times Cited: 3

Keywords

  • Exterior durability, Materials, Weathering stress, Chain scission, Accelerated testing, Network degradation
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

Download statistics

No data available

ID: 51174768