Microstructural investigation of the oxide formed on TP 347H FG during long-term steam oxidation

Publication: Research - peer-reviewJournal article – Annual report year: 2010

View graph of relations

The long-term oxidation behaviour of TP347H FG in ultra supercritical steam conditions was assessed by exposing the steel in test superheater loops in a Danish coal-fired power plant and characterising the oxide layer with reflective light and electron microscopy. Double layered oxide scales formed during steam oxidation. TEM investigations reveal that the inner oxide layer consists of particles of metallic Ni/Fe and Fe-Cr spinel in the interior of the former alloy grains and a compact layer of Fe-Cr spinel and Cr2O3 along the former alloy grain boundaries. The morphology suggests that the inner layer grows by internal oxidation of the interior of the alloy grains. The thickness of the inner oxide layer did not change significantly with oxidation time and temperature for exposure times up to 30 000 h. Faster Cr diffusion within the fine-grained alloy at higher temperatures is held responsible for this observation. This hypothesis is supported by kinetic data. The oxide thickness at low and high temperatures after 58 000 h exposure was higher than expected.
Original languageEnglish
JournalMaterials and Corrosion
Publication date2010
Volume61
Issue8
Pages665-675
ISSN0947-5117
DOIs
StatePublished
CitationsWeb of Science® Times Cited: 3
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

ID: 5451453