Mechanical processing of bast fibres: The occurrence of damage and its effect on fibre structure

Publication: Research - peer-reviewJournal article – Annual report year: 2012

View graph of relations

Currently, separation processes used for natural fibres for composite reinforcing textiles cause a significant amount of damage to the fibres. Microscopic analysis showed that industrially processed flax (Linum usitassimium L.) fibres contained significantly more defects than green or retted ones and that further mechanical processing did not significantly increase the amount of defects. In this study it has been shown, by analysing the degree of polymerisation of cell wall components indirectly by viscosity measurements, that mechanically induced defects do not significantly cleave the cell wall polymers. Acid hydrolysis, however, induced more degradation of the cell wall polymers in fibres having a greater degree of damage, indicating that that defects are more susceptible to certain chemical reactions and which in turn might cause problems for example, during chemical modification of fibres due to heterogeneous reactivity. Analogous findings were observed in hemp (Cannabis sativa L.) fibre damaged in the laboratory under controlled conditions, emphasising the need to develop extraction and separation processes that minimise mechanical damage to the fibres.
Original languageEnglish
JournalIndustrial Crops and Products
Publication date2012
Volume39
Pages7-11
ISSN0926-6690
DOIs
StatePublished
CitationsWeb of Science® Times Cited: 4

Keywords

  • Natural fibre, Mechanical processing, Defects, Hemp, Flax
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

ID: 7726305