Instantaneous monitoring of wear on a micro-nanometer scale through hard coatings by synchroton radiation

Publication: Research - peer-reviewConference abstract for conference – Annual report year: 2010

Documents

View graph of relations

We have shown that wear dynamics can be monitored on a lateral micrometer scale by synchrotron radiation. We have followed the wear from the change in transmission on a system of three layers of hard coatings, TiAlN, CrN and TiAlN, of approximately one micron thickness produced by sputtering deposition. These layers were deposited on a 1 mm-thick vitreous carbon sample. The instantaneous depth was determined from transmission as well as XANES (X-ray Absorption Near Edge Spectra) measurements of the K-edge of Cr from the-CrN marker layer. The wear process is highly irregular and the local wear rate varies strongly from one position to another in the wear track. The ridges, grooves as well as the transport of debris from the track were for the first time followed on a micrometer level, confirming the stochastic nature of this type of wear. Most of the features are generated within the first 500 nm and exist over several micrometers. However, also a significant fraction of grooves and ridges disappear by wear over less than one micrometer.
Original languageEnglish
Publication date2010
StatePublished

Conference

Conference2010 Dansk Fysisk Selskabs Årsmøde
CountryDenmark
CityNyborg
Period22/06/1023/06/10
Internet addresshttp://www.dfs.nbi.dk/aarsmoeder/2010/aarsmoede.php
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

Download statistics

No data available

ID: 5245116