Influence of Bi, Se and Te additions on the formation temperature of MgB2

Publication: Research - peer-reviewJournal article – Annual report year: 2011

View graph of relations

The formation of the MgB2 superconducting compound from a mixture of Mg and amorphous B powders with various low melting point metals (Bi, Se and Te) was studied in situ by means of high-energy (synchrotron) x-ray diffraction in wires with a composite Cu/Nb sheath. In comparison with an undoped sample, it was found that the addition of Bi results in a clear lowering of the formation temperature of MgB2, whereas Se and Te have no significant influence. Tc is slightly higher in the Bi-doped sample than in the others but the jc in this case is lower than in the pure MgB2 sample, probably due to the presence of remaining Mg3Bi2 particles that formed as an intermediate compound during reaction. Likewise, in the Se-and Te-doped samples, MgSe and MgTe respectively form below 450 °C. Whereas jc is also depressed in the Se-doped sample, the MgTe particles do not appear to affect the performance of the Te-doped wire.
Original languageEnglish
JournalSuperconductor Science & Technology
Publication date2012
Volume25
Issue1
Pages015010
ISSN0953-2048
DOIs
StatePublished
CitationsWeb of Science® Times Cited: 5
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

ID: 6310739