In vitro studies of PEG thin films with different molecular weights deposited by MAPLE

Publication: Research - peer-reviewJournal article – Annual report year: 2012

View graph of relations

In this work, polyethylene glycol (PEG) films were produced by Matrix Assisted Pulsed Laser Evaporation (MAPLE). The possibility to tailor the properties of the films by means of polymer molecular weight was explored. The films of PEG of average molecular weights 400 Da, 1450 Da, and 10000 Da (PEG400, PEG1450, and PEG10000) were investigated in vitro, in media similar with those inside the body (phosphate buffer saline PBS with pH 7.4 and blood). The mass of the polymer did not change during this treatment, but the polymer molecular weight was found to strongly influence the films properties and their behavior in vitro. Thus, immersion in PBS induced swelling of the PEG films, which was more pronounced for PEG polymers of higher molecular weight. Prior to immersion in PBS, the PEG films of higher molecular weight were more hydrophilic, the water contact angles decreasing from ∼66 grd for PEG400 to ∼41 grd for PEG 1450 and to ∼15 grd for PEG10000. The same trend was observed during immersion of the PEG films in PBS. Before immersion in PBS, the refractive index of the films increased from ∼1.43 for PEG400 to ∼1.48 for PEG1450 and to ∼1.68 for PEG10000. During immersion in PBS the refractive index decreased gradually, but remained higher for the PEG molecules of higher mass. Finally, blood compatibility tests showed that the PEG films of higher molecular weight were most compatible with blood. © 2012 Springer-Verlag.
Original languageEnglish
JournalApplied Physics A
Publication date2012
Volume109
Issue1
Pages223-232
ISSN0947-8396
DOIs
StatePublished
CitationsWeb of Science® Times Cited: 1

Keywords

  • Blood, Contact angle, Molecular weight, Polyethylene glycols, Polymers, Refractive index, Polymer films
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

ID: 12365433