In situ investigation of the martensitic transformation in Fe–12 wt.%Ni–0.6 wt.%C steel at subzero temperatures

Publication: Research - peer-reviewJournal article – Annual report year: 2012

View graph of relations

Martensitic transformation in a Fe–12 wt.%Ni–0.6 wt.%C alloy was investigated with magnetometry and in situ (synchrotron) X-ray diffraction at sub-zero Celsius temperature. In situ X-ray diffraction at the HZBBESSY II synchrotron facility was applied to quantitatively determine the fractions of retained austenite and martensite formed during: (i) isochronal transformation, while cooling at a rate of 3 K/min from room temperature to 138 K, and (ii) isothermal transformation, while holding at 138 K. X-ray diffraction analysis was also used for a qualitative evaluation of the stress evolution in austenite during the transformation. Magnetometry was applied to monitor the overall kinetics for the same isochronal and
isothermal transformations. The results are discussed in the light of the current theories on martensitic
transformations.
Original languageEnglish
JournalJournal of Alloys and Compounds
Publication date2013
Volume577
Journal numberSupplement 1
PagesS543-S548
ISSN0925-8388
DOIs
StatePublished
CitationsWeb of Science® Times Cited: 0

Keywords

  • Phase transformation, Magnetometry, X-ray diffraction, Martensite, Retained austenite
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

ID: 9748824