New amorphous interface for precipitate nitrides in steel

Publication: Research - peer-reviewJournal article – Annual report year: 2014

View graph of relations

According to classical theories precipitate interfaces are described by their degree of coherency with the matrix, which affects their strengthening contribution. Investigations of nitride precipitate interfaces in 12% Cr steels with transmission electron microscopy have shown the nitrides to be enveloped in an amorphous shell a few nm thick, thus leaving them without any coherency with the matrix. The amorphous nature of the shells could be ascertained with high resolution microscopy and dark field techniques. When extracted from the ferrite matrix the amorphous shells were observed to crystallize during electron beam exposure. The amorphous shells were observed around Ta- and Nb-based nitrides, which are considered to have a high interfacial energy with the ferrite matrix. They were not observed around V-based nitrides which have a Baker–Nutting relationship with low-misfit to the matrix.
Original languageEnglish
JournalPhilosophical Magazine (London, 2003)
Volume94
Issue number20
Pages (from-to)2339-2349
ISSN1478-6435
DOIs
StatePublished - 2014
CitationsWeb of Science® Times Cited: 2

    Keywords

  • Amorphous, Interface, Precipitate
Download as:
Download as PDF
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
Word

ID: 92546819