In this work, nanostructured (La0.6Sr0.4)0.99CoO3 (LSC)-Ce0.8Gd0.2O1.9 (CGO) core-shell particles were prepared by precipitating CGO nanoparticles on the surface of LSC particles under hydrothermal conditions. The as-prepared core-shell particles were sintered by spark plasma sintering (SPS) and conventional sintering, and the microstructure evolution and densification behavior were studied. Dense microstructures were reached using both sintering methods at relatively low temperatures. In the case of SPS, the core-shell architecture was partially maintained and nano-structured CGO grains were formed, while conventional sintering led to the formation of larger CGO grains. This work covers a detailed characterization of (a) the individual LSC-CGO core-shell particles and (b) the composites after densification.
Original languageEnglish
JournalCeramics
Volume1
Issue number2
Pages (from-to)246-260
ISSN2571-6131
DOIs
StatePublished - 2019
CitationsWeb of Science® Times Cited: No match on DOI

    Research areas

  • Hydrothermal, Core-shell, Lanthanum strontium cobaltite, Gadolinium-doped ceria, Spark plasma sintering
Download as:
Download as PDF
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
Word

Download statistics

No data available

ID: 165719804