High-Performance Microchanneled Asymmetric Gd0.1Ce0.9O1.95-δ-La0.6Sr0.4FeO3-δ-Based Membranes for Oxygen Separation

Publication: Research - peer-reviewJournal article – Annual report year: 2016

DOI

View graph of relations

A microchanneled asymmetric dual phase composite membrane of 70 vol % Gd0.1Ce0.9O1.95-delta-30 vol % La0.6Sr0.4FeO3-delta (CGO-LSF) was fabricated by a "one step" phase-inversion tape casting. The sample consists of a thin dense membrane (100 mu m) and a porous substrate including "finger-like" microchannels. The oxygen permeation flux through the membrane with and without catalytic surface layers was investigated under a variety of oxygen partial pressure gradients. At 900 degrees C, the oxygen permeation flux of the bare membrane was 1.6 (STP) ml cm(-2) min(-1) for the air/He-case and 10.10 (STP) ml cm(-2) min(-1) for the air/CO-case. Oxygen, flux measurements as well as electrical conductivity relaxation show that the oxygen flux through the bare membrane without catalyst is limited by the oxygen surface exchange. The surface exchange can be enhanced by introduction of catalyst on the membrane surface. An increase of the 50 150 oxygen flux of-4.49 (STP) mL cm(-2) min(-1) at 900 degrees C was observed when catalyst is added for the air/He-case. Mass transfer polarization through the finger-like support was confirmed to be negligible, which benefits the overall performance. A stable flux of 7.00 (STP) ml cm(-2) min(-1) was observed between air/CO/CO2 over 200 h at 850 degrees C. Partial surface decomposition was observed on the permeate side exposed to CO, in line with predictions from thermodynamic calculations. In a mixture of CO, CO2, H-2, and H2O at similar oxygen activity the material will according to the calculation not decompose. The microchanneled asymmetric CGO-LSF membranes show high oxygen permeability and chemical stability under a range of technologically relevant oxygen potential gradients.
Original languageUndefined/Unknown
JournalA C S Applied Materials and Interfaces
Volume8
Issue number7
Pages (from-to)4548-4560
Number of pages13
ISSN1944-8244
DOIs
StatePublished - 2016
CitationsWeb of Science® Times Cited: 4

    Keywords

  • Phase inversion, Dual-phase composite membranes, Electrical conductivity relaxation, Surface exchange, Mass transfer polarization, Thermodynamic calculation

Projects

Download as:
Download as PDF
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
Word

ID: 122944204