Highly porous Ce-W-TiO2 free-standing electrospun catalytic membranes for efficient de-NOx via ammonia selective catalytic reduction

Research output: Contribution to journalJournal article – Annual report year: 2019Researchpeer-review

DOI

View graph of relations

Highly porous Ce-W-TiO2 free-standing nanofibrous membranes (FSM) are fabricated via electrospinning techniques to serve as NOx-SCR catalysts. The precursor of the ceramic nanofibers (sol-gel solution) is co-electrospun with a poly(vinyl alcohol) (PVA) water solution. PVA integration into FSM is proven to avoid excessive bending of the nanofibers, and to prevent mechanical failure of the final ceramic nanofibrous structure. This is demonstrated to be associated with PVA higher thermal stability compared with the other organic additives. 3D tomography reconstruction indicates a resulting ceramic membrane with a great open and interconnected porosity of ca. 96%. The catalytic characterization, performed at the best working conditions (in absence of H2O and SO2), indicates the amorphous FSM as the best performing catalytic membrane. Superior catalytic performances for the developed FSM, over the nanofibers and the nanoparticles catalysts are proven, as a result of superior surface, morphological, and structural features. Long-term stability (120 h) and reproducibility (over 5 cycles) of the FSM are also demonstrated.
Original languageEnglish
JournalEnvironmental Science: Nano
Volume6
Issue number1
Pages (from-to)94-104
ISSN2051-8153
DOIs
Publication statusPublished - 2019
CitationsWeb of Science® Times Cited: No match on DOI
Download as:
Download as PDF
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
Word

ID: 159957709