High temperature proton exchange membranes based on polybenzimidazole and clay composites for fuel cells

Publication: Research - peer-reviewJournal article – Annual report year: 2011

NullPointerException

View graph of relations

dispersion of modified laponite clay was achieved in polybenzimidazole (PBI) solutions which, when cast and allowed to dry, resulted in homogeneous and transparent composite membranes containing up to 20 wt% clay in the polymer. The clay was organically modified using a series of ammonium and pyridinium salts with varying polarity and hydrogen-bonding capacity. Clay modification by ion-exchange reactions involving replacement of interlayer inorganic cations was confirmed using X-ray photoelectron and infrared spectroscopy techniques. The cast PBI membranes were characterized by their water uptake, acid doping and swelling, tensile strength, conductivity and hydrogen permeability as well as by fuel cell tests. For the composite membranes, high acid doping levels were achieved with sufficient mechanical strength and improved dimensional stability or reduced membrane swelling. At an acid doping level of 12 mol H3PO4 per monomer unit, proton conductivity as high as 0.12 S cm−1 was obtained at 150 °C and 12% relative humidity. The composite membranes exhibited hydrogen permeability ranging from 0.6 to 1.2 × 10−10 mol cm−1 s−1 bar−1 from 100 to 200 °C, which was five times lower than that of acid-doped pristine PBI membranes. In accordance with the hydrogen permeability measurements, fuel cell tests exhibited high open circuit voltages (i.e., 1.02 V) at room temperature as well as high I–V performance compared with normal PBI membranes.
Original languageEnglish
JournalJournal of Membrane Science
Publication date2011
Volume383
Journal number1-2
Pages78-87
ISSN0376-7388
DOIs
StatePublished
CitationsWeb of Science® Times Cited: 11

Keywords

  • Permeability, Bio polymers, Clay, Polybenzimidazole (PBI), Conductivity, Tensile strength, High temperature PEMFC, Composite membranes
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

ID: 6327917