Publication: Research - peer-review › Journal article – Annual report year: 2009
The present article considers forward extrusion, closed-die forging and backward extrusion processes for fabrication of individual microcomponents from two bulk metallic glass (BMG) compositions: Mg60Cu30Y10 and Zr44Cu40Ag8Al8. Two types of tooling were used in the present work: relatively massive die sets characteristic of cold forming operations for crystalline metals and lightweight die sets adapted to the special characteristics of BMGs. In addition to demonstrating that microcomponents of several geometries can be readily fabricated from BMGs, rheological properties are combined with crystallization kinetics to formulate a generally applicable method that can guide selection of optimal forming parameters. Finally, the use of particulate-based lubricants for BMG forming is shown to result in individual lubricant particles becoming mechanically locked into the BMG surface. (C) 2008 Elsevier B.V. All rights reserved.
|Journal||Journal of Materials Processing Technology|
|State||Published - 2009|
|Citations||Web of Science® Times Cited: 12|
- Materials research