Feeding and Distribution of Porosity in Cast Al-Si Alloys as Function of Alloy Composition and Modification

Publication: Research - peer-reviewJournal article – Annual report year: 2012

View graph of relations

Unmodified, Na-modified, and Sr-modified castings of Al-7 pct Si and Al-12.5 pct Si alloys were cast in molds in which it was possible to create different cooling conditions. It is shown how solidification influences the distribution of porosity at the surface and the center of the castings as a function of modification and Si content in sand- and chill-cast samples. Eutectic modification, Si content, and cooling conditions have a great impact on the distribution of porosity. Unmodified and Na-modified castings are more easily fed with porosity tending to congregate near the centerline of the casting, while Sr-modified castings solidify in a mushy manner that creates a more homogeneous distribution of porosity in the casting. The amount of porosity was highest in the Sr-modified alloys, lower in the Na-modified alloys, and lowest in the unmodified alloys. The size of the porosity-free layer and the effectiveness of the feeders were greater in the castings made with the steel chills due to the increased thermal gradients and consequent increase in the directionality of solidification.
Original languageEnglish
JournalMetallurgical and Materials Transactions A - Physical Metallurgy and Materials Science
Publication date2012
Volume43
Issue12
Pages4846-4858
ISSN1073-5623
DOIs
StatePublished

Bibliographical note

© The Minerals, Metals & Materials Society and ASM International 2012

CitationsWeb of Science® Times Cited: 4
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

Download statistics

No data available

ID: 12630483