## Fabrication of the Textured Ni-9.3at.%W Alloy Substrate for Coated Conductors

Publication: Research - peer-reviewJournal article – Annual report year: 2011

### Standard

Fabrication of the Textured Ni-9.3at.%W Alloy Substrate for Coated Conductors. / Gao, M. M.; Suo, H. L.; Grivel, Jean-Claude; Yue, Zhao; Gao, P. K.; Liu, M.; Ma, L.

In: I E E E Transactions on Applied Superconductivity, Vol. 21, No. 3, 2011, p. 2969-2972.

Publication: Research - peer-reviewJournal article – Annual report year: 2011

### Author

Gao, M. M.; Suo, H. L.; Grivel, Jean-Claude; Yue, Zhao; Gao, P. K.; Liu, M.; Ma, L. / Fabrication of the Textured Ni-9.3at.%W Alloy Substrate for Coated Conductors.

In: I E E E Transactions on Applied Superconductivity, Vol. 21, No. 3, 2011, p. 2969-2972.

Publication: Research - peer-reviewJournal article – Annual report year: 2011

### Bibtex

@article{ab38977c70a546d191931b660943bc40,
title = "Fabrication of the Textured Ni-9.3at.%W Alloy Substrate for Coated Conductors",
keywords = "Materials characterisation and modelling, Materialekarakterisering og modellering",
author = "Gao, {M. M.} and Suo, {H. L.} and Jean-Claude Grivel and Zhao Yue and Gao, {P. K.} and M. Liu and L. Ma",
note = "Copyright 2010 IEEE. Personal use of this material is permitted. However, permission to reprint/republish this material for advertising or promotional purposes or for creating new collective works for resale or redistribution to servers or lists, or to reuse any copyrighted component of this work in other works must be obtained from the IEEE.",
year = "2011",
doi = "10.1109/TASC.2011.2105850",
volume = "21",
pages = "2969--2972",
journal = "I E E E Transactions on Applied Superconductivity",
issn = "1051-8223",
publisher = "Institute of Electrical and Electronics Engineers",
number = "3",

}

### RIS

TY - JOUR

T1 - Fabrication of the Textured Ni-9.3at.%W Alloy Substrate for Coated Conductors

AU - Gao,M. M.

AU - Suo,H. L.

AU - Grivel,Jean-Claude

AU - Yue,Zhao

AU - Gao,P. K.

AU - Liu,M.

AU - Ma,L.

N1 - Copyright 2010 IEEE. Personal use of this material is permitted. However, permission to reprint/republish this material for advertising or promotional purposes or for creating new collective works for resale or redistribution to servers or lists, or to reuse any copyrighted component of this work in other works must be obtained from the IEEE.

PY - 2011

Y1 - 2011

N2 - It is difficult to obtain a sharp cube texture in the Ni-9.3at.% W substrate used for coated conductors due to its low stacking fault energy. In this paper, the traditional cold rolling procedure was optimized by introducing an intermediate recovery annealing. The deformation texture has been improved after three recovery annealing cycles at 500$^{\circ}{\rm C}$ for 2 h during the cold rolling process. After optimized recrystallization annealing, a Ni-9.3at.% substrate with a cube texture content of 87.7% $( has been obtained. The effect of the intermediate annealing on cube texture formation is attributed to the improved deformation texture and to the enhanced pre-existing cube oriented structure in the deformed matrix. AB - It is difficult to obtain a sharp cube texture in the Ni-9.3at.% W substrate used for coated conductors due to its low stacking fault energy. In this paper, the traditional cold rolling procedure was optimized by introducing an intermediate recovery annealing. The deformation texture has been improved after three recovery annealing cycles at 500$^{\circ}{\rm C}$for 2 h during the cold rolling process. After optimized recrystallization annealing, a Ni-9.3at.% substrate with a cube texture content of 87.7%$( has been obtained. The effect of the intermediate annealing on cube texture formation is attributed to the improved deformation texture and to the enhanced pre-existing cube oriented structure in the deformed matrix.

KW - Materials characterisation and modelling

KW - Materialekarakterisering og modellering

U2 - 10.1109/TASC.2011.2105850

DO - 10.1109/TASC.2011.2105850

M3 - Journal article

VL - 21

SP - 2969

EP - 2972

JO - I E E E Transactions on Applied Superconductivity

T2 - I E E E Transactions on Applied Superconductivity

JF - I E E E Transactions on Applied Superconductivity

SN - 1051-8223

IS - 3

ER -