Evolution of microstructure and hardness of AE42 alloy after heat treatments

Publication: Research - peer-reviewJournal article – Annual report year: 2008

View graph of relations

The AE42 magnesium alloy was developed for high pressure die casting (HPDC) from low-aluminum magnesium alloys. In this alloy the rare earth (RE) elements were shown to increase creep resistance by forming AlxREy intermetallics along the grain boundaries. The present work investigates the microstructure of squeeze cast AE42 magnesium alloy and evaluates its hardness before and after heat treatments. The change in hardness is discussed based on the microstructural observations. Some suggestions are given concerning future design of alloy compositions in order to improve high temperature creep properties even further. It is shown that the microstructure of the squeeze-cast AE42 alloy is stable at high temperature 450 degrees C. The subsequent solution and ageing treatments have a limited effect on the hardness. The weak age-hardening is attributed to the precipitation of small amount Of Mg17Al12-phase with the use of about 0.7 wt.% aluminum. The heat treatment to achieve a maximum increase in the hardness is: solution treatment at 450 degrees C for 5-10 h followed by an ageing treatment at 190-220 degrees C for about 5 It. (C) 2007 Elsevier B.V. All rights reserved.
Original languageEnglish
JournalJournal of Alloys and Compounds
Publication date2008
Volume463
Issue1-2
Pages238-245
ISSN0925-8388
DOIs
StatePublished
CitationsWeb of Science® Times Cited: 17
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

ID: 3251726