Electrochemical behaviour of (La1-xSrx)(s)Co1-yNiyO3-δ as porous SOFC cathodes

Publication: Research - peer-reviewJournal article – Annual report year: 2009

View graph of relations

This paper shows that storage at room temperature and ambient atmosphere appears to affect the polarisation resistance significantly and RP decreased initially with storage time. This improvement was more pronounced when stored in moisturised air. The performance was, however, also found to decrease when stored for sufficiently long periods. The absolute values of the electrode response of these materials are very difficult to reproduce and the performance appears to be largely dependent on the manufacturing process of the powder or the electrode itself. In spite of this, the electrode behaviours exhibited similar patterns with respect to the dependence on T and PO2. An increase in polarisation resistance with time at SOFC operating conditions was observed, which was related exclusively to the electrode reaction kinetics and not to oxygen concentration polarisation. It was also found to be higher when measured in moisturised air.
Original languageEnglish
JournalSolid State Ionics
Publication date2009
Volume180
Issue26-27
Pages1395-1405
ISSN0167-2738
DOIs
StatePublished
CitationsWeb of Science® Times Cited: 18

Keywords

  • Solid Oxide Fuel Cells, Fuel Cells and hydrogen
Download as:
Download as PDF
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBEHarvardMLAStandardVancouverShortLong
Word

ID: 4325761