Electrocatalytic properties of Ti/Pt–IrO2 anode for oxygen evolution in PEM water electrolysis

Publication: Research - peer-reviewJournal article – Annual report year: 2010

View graph of relations

A novel Pt–IrO2 electrocatalyst was prepared using the dip-coating/calcinations method on titanium substrates. Titanium electrodes coated with oxides were investigated for oxygen evolution. Experimental results showed that Ti/Pt–IrO2 electrode containing 30mol% Pt in the coating exhibited significantly higher electrocatalytic activity for oxygen evolution compared to Ti/IrO2 prepared by the same method, which is also supported by the electrochemical impedance data. Stability tests demonstrated Pt–IrO2 electrocatalyst had a service cycle of 10,000 times in 0.1M H2SO4 solution. And the anode surface had hardly discovered cracks and had compact structures, which contributed to stable nature of the electrode together with good conductivity and specific interaction between Pt and IrO2 formed during the calcination. Furthermore, the enhanced catalytic activity for O2 evolution at Ti/Pt–IrO2 electrode is preliminarily discussed using the Mott–Schottky analysis.
Original languageEnglish
JournalInternational Journal of Hydrogen Energy
Volume35
Issue number15
Pages (from-to)8049-8055
ISSN0360-3199
DOIs
StatePublished - 2010
Peer-reviewedYes
CitationsWeb of Science® Times Cited: 21

Keywords

  • Pt–IrO2, Oxygen evolution reaction, Water electrolysis, Catalytic activity
Download as:
Download as PDF
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
PDF
Download as HTML
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
HTML
Download as Word
Select render style:
APAAuthorCBE/CSEHarvardMLAStandardVancouverShortLong
Word

ID: 5217475